An experimental investigation of the impact response and post-impact shear buckling behaviour of hybrid composite laminates

Damghani, Mahdi; Saddler, John; Sammon, Ethan; Atkinson, Gary A.; Matthews, Jason; Murphy, Adrian

Abstract

This paper investigates the effect of transverse impact loading on the in-plane shear behaviour of two laminate configurations. The extensive experimental studies consider a pure carbon laminate (type 1) and a novel X-shaped carbon/glass laminate (type 2). The results establish that all three graduated impact energy levels (5J, 7.5J and 10J) induce through-thickness matrix cracking, fibre breakage and delamination in the type 1 laminate. However, the use of glass plies in the type 2 laminates resulted in only matrix cracking towards the impacted surface and limited through-thickness damage. Post impact, both laminate types demonstrated lower buckling load, failure load and stiffness. The reduction in buckling load of the type 1 specimens was greater than that of the type 2 specimens. However, the reduction in failure load of the type 1 specimens was less than that seen in the type 2 specimens. Both laminate types demonstrated a stable post-buckling equilibrium path. A novel machine vision technique based on polarisation imaging was successful in standardising the process of identifying the damage location/size for the type 1 laminates, but not for the type 2 laminates. This was due to the inclusion of surface glass plies which, unlike carbon plies, do not polarise light at the point of reflection.

• Journal Article Type: Article
• Acceptance Date: Nov 24, 2022
• Publication Date: Feb 1, 2023
• Deposit Date: Nov 28, 2022
• Publicly Available Date: Nov 29, 2022
• Journal: Composite Structures
• Print ISSN: 0263-8223
• Publisher: Elsevier
• Peer Reviewed: Peer Reviewed
• Volume: 305
• Pages: 116506
• DOI: https://doi.org/10.1016/j.compstruct.2022.116506
• Keywords: Composite laminates; Low velocity impact ;Shear loading ;Impact behaviour
• Public URL: https://uwe-repository.worktribe.com/output/10194634
• Publisher URL: https://www.sciencedirect.com/science/article/pii/S0263822322012387